Method of making media of controlled porosity and product thereof

ABSTRACT

A method of making a non-woven fibrous media, combining high vapor permeability and low liquid permeability, includes the steps of providing a non-woven fabric formed from fibers that are prematurely crystallized during fabric formation and have a wide heat of fusion range distribution, and calendering the fabric to soften the small polymer crystals therein of low heats of fusion, but not the relatively larger polymer crystals therein of relatively higher heats of fusion, thereby to retain high vapor permeability while providing low liquid permeability. The polymer is preferably isotactic polypropylene.

BACKGROUND OF THE INVENTION

[0001] The present invention relates to a method of making fibrous media of controlled porosity, and more particularly such a media which combines high vapor permeability and low liquid permeability, and the product thereof.

[0002] It is well known to produce a laminate made from various polymers and textiles for use in a wide variety of product applications. For example, meltblown and spunbond materials afford a high level of vapor permeability and liquid permeability when used either by themselves or in combination with one another and/or other porous materials.

[0003] Meltblowing is a method for economically producing very small fibers which are mostly suitable for filtration and insulation applications. Fibers smaller than 1 micron in diameter may be produced by meltblowing, and the average fiber diameter in conventional meltblowing is about 4 microns, with fiber size distribution ranging from ¼micron to 8 microns. To form such small fibers one must start with polymer resins of very low molecular weight. In this process the nonwoven fabric is formed in one step from the polymer resin into the final meltblown nonwoven fabric.

[0004] In contrast, spunbonding is very similar to conventional fiber spinning where several processing steps are required to form the spunbond fabric. Spunbond fibers go through a drawing stage and then a laydown stage wherein the drawn fibers are laid down into a matt and the matt is then bonded by a thermobonding calender or mechanical entangling to form the nonwoven fabric. The resins used in the spunbonding process have lower molecular weight than those used in the conventional melt spinning process and higher molecular weights than those used in the conventional meltblowing process. Fibers smaller than 10 microns in diameter are very difficult to produce economically by spunbonding, and the average fiber diameter for conventional spunbonding processes is about 18 microns.

[0005] However, for particular applications, such as those in the health care industry—e.g., infant diapers, sanitary pads, adult incontinence wear, medical surgical dressings, and the like—the laminate must perform three distinct functions: First, a topsheet intended to contact the patient's skin must allow the passage of moisture (e.g., blood, urine and like liquids) therethrough while at the same time providing an acceptable feel to the wearer's skin. Second, an absorbent core, intermediate the topsheet and the backsheet, must be capable of absorbing the moisture which has been received through the frontsheet. Third, a backsheet, on the back of the absorbent core, prevents leakage of moisture outwardly of the laminate. The present invention relates specifically to the backsheet component.

[0006] The barrier properties of the backsheet (i.e., the trapping of moisture and other liquids) are typically achieved by incorporating into the backsheet a plastic layer or film which acts as a moisture barrier. Various major disadvantages associated with the utilization of such barrier films are the low moisture vapor transmission rates (MVTR) of the barrier films, undesirable crinkling noise created by the barrier film during usage of the product, and a stiffening of the product (due to the barrier film) which reduces its conformability to the area to which it is applied.

[0007] Porous films are typically permeable to both liquid water and water vapor. They may be made by the incorporation of different organic or inorganic additives into a polymer film, the film then being stretched or fillers removed therefrom chemically. Other conventional methods include mechanical perforation and/or radiation techniques to form the desired holes or slits in the polymeric film. Formation of uniform pore size in a film is very difficult, and porous plastic films are generally more expensive than non-wovens.

[0008] On the other hand, non-porous barrier films are typically impermeable to both liquid water and water vapor. As a result, using the impermeable film in a diaper backsheet, for example, makes the diaper hot before exposure to liquid (as the barrier film prevents air circulation) and clammy after exposure to moisture (because the barrier film precludes moisture evaporation). Indeed, the use of an impermeable barrier film in a diaper may cause severe dermatological problems, such as skin rash on infants, and skin sores on adults wearing such non-porous products.

[0009] It is also known to form a semi-porous barrier film of controlled porosity which is permeable to water vapor, but impermeable to liquid water—that is, breathable. However, the method of manufacturing such a microporous film of controlled porosity is typically complex and expensive, and requires a relatively specialized polymeric input (for example, conjugate fibers formed of two separately manufactured polymeric materials or laminates formed of two separately manufactured polymeric materials).

[0010] Clearly the need remains for a method of economically manufacturing a media of controlled porosity, combining high vapor permeability and low liquid permeability, without the use of chemical binders, additives or coatings, from a single commercially available polymer. Such breathable media would find use in products which are sold in such quantity that any reduction in the cost thereof (e.g., which makes it sufficiently economical for manufacture for use in disposable products) is highly desirable.

[0011] Accordingly, it is an object of the present invention to provide a method of making of a media of controlled porosity, combining high vapor permeability and low liquid permeability.

[0012] Another object is to provide such a method which does not require a specialized polymeric input.

[0013] A further object is to provide such a method which does not require the use of chemical binders, additives or coatings to provide the desired permeability or porosity.

[0014] It is also an object of the present invention to provide a material made by the aforesaid method.

[0015] It is another object to provide such a material which does not produce noise during use and which exhibits cloth-like feel (hand).

[0016] It is a further object to provide such a material which is economical to manufacture (e.g., for use in disposable products).

SUMMARY OF THE INVENTION

[0017] It has now been found that the above and related objects of the present invention are obtained in a method of making a non-woven fibrous media combining high vapor permeability and low liquid permeability. The method comprises the steps of providing a non-woven fabric formed from fibers that are prematurely crystalized during web formation and have a wide heat of fusion range distribution, and then calendering the fabric to soften the small polymer crystals therein of low heats of fusion, but not the relatively larger crystals therein of relatively higher heats of fusion, thereby to retain high vapor permeability.

[0018] The present invention additionally comprises a non-woven fibrous media providing high vapor permeability and low liquid permeability. The material is a non-woven fabric formed from fibers that are prematurely crystalized polymer and have a wide heat of fusion range distribution. The fabric is calendered to soften the small polymer crystals therein of low heats of fusion, but not the relatively large polymer crystals therein of relatively higher heats of fusion, thereby to retain high vapor permeability while providing low liquid permeability.

[0019] In a preferred embodiment the polymer is polypropylene, and optimally isotactic polypropylene, although other isotactic polymers may be used. The polymer is prematurely crystalized, preferably by quenching it prior to completion of fiber structural formation so that the polymer exhibits a bell-shaped heat of fusion range distribution (prior to calendering). The temperature, pressure and roller speed of the calendering operation are selected to soften the small polymer crystals, but not the relatively larger polymer crystals. For example, the fabric is preferably calendered at a temperature of about 25-110° C., a pressure of about 25-150 Newtons, and a roller speed of up to 200 meters/minute. The fabric is calendered to retain a moisture vapor permeability of at least about 1200 g/m² @ 24 hours and to provide a hydrostatic head of at least about 10 millibars (about 100 mm H₂O). The calendered material may be made into a composite with, for example, at least one spunbond, spunmelt or other nonwoven fabric layer.

BRIEF DESCRIPTION OF THE DRAWING

[0020] The above and related objects, features and advantages of the present invention will be more fully understood by reference to the following detailed description of the presently preferred, albeit illustrative, embodiments of the present invention when taken in conjunction with the accompanying drawing wherein:

[0021]FIG. 1 is an isometric view of a fabric according to the present invention, laminated to a spunbond fabric, for use in a diaper; and

[0022]FIG. 2 is a flow chart of a preferred method of making the fabric.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

[0023] Referring now to the drawing, and in particular to FIGS. 1 and 2 thereof, the present invention relates to a method of making a non-woven fibrous media of controlled porosity, generally designated by the reference numeral 10 the media combining high vapor permeability and low liquid permeability. While for the purposes of the present invention, the media will be described as combining high water vapor permeability and low liquid water permeability, clearly the intended application of the media will dictate the specifics of these criteria—for example, whether the low liquid permeability applies to blood, bodily exudate or like liquids and whether the high vapor permeability applies to water vapor, air or like gases. Typically, the goal is a substantially water liquid impermeable and substantially water vapor permeable media. The optimum balance of properties can be tailored for individual applications.

[0024] The molten polymer from which the media will be made is preferably isotactic in nature so that it has a uniform structure over its polymeric chain length. Alternatively, however, syndiotactic polymer may be used in particular applications where the uniformity of the structure is of lesser importance. Atactic materials are not suitable for the purpose of the present invention since the structure thereof is so irregular over its polymeric chain length that they strongly resist crystallization. Polyolefins are preferred for use as the polymer, polypropylene being especially preferred. Thus, the preferred polymer for use in the present invention is isotactic polypropylene.

[0025] Typically, pellets or other conventional forms of the polymer suitable for handling within a manufacturing plant are placed in the hopper of a spinnerette and melted through an extruder. Once molten, the polymer is forced (extruded) through a spinnerette die defining small nozzles through which the molten polymer passes, thereby forming fibers as the polymer cools. For ease of processing, the polymer preferably has a very high melt flow level rate and is collected from the spinnerette die at very close die-collector distances. While the non-woven fabric is preferably a meltblown, it may also be a spunbond or other non-woven fibrous media to the extent that a suitable fabric is produced.

[0026] It is a feature of the present invention that the fabric be formed from fibers that are prematurely crystalized during fabric formation. Such prematurely crystalized fibers exhibit a “smectic” crystalline structure. A smectic crystalline structure contains both small polymer crystals of low heat of fusion and relatively larger polymer crystals of relatively higher heats of fusion. The smectic crystalline structure is also referred to as “paracrystallinity.”

[0027] The smectic or prematurely crystalized nature of the fibers useful in the method of the present invention can be achieved in a variety of different ways. The most common technique is to quench the fibers emerging from the spinnerette die (e.g., with a cold gas or liquid, such as air below 23° C.) before all of the polymer crystals in the fibers have grown to their full extent. As a result, the quenched fibers will contain small polymer crystals of low heats of fusion and relatively larger polymer crystals of relatively higher heat suffusion. In other words, prematurely crystalized fibers exhibit a wide range distribution of the heats of fusion.

[0028] That the polymer fibers exhibit a relatively wide heats of fusion distribution is evidenced by the relatively broad bell-shaped curve distribution observed in the DSC (Differential Scanning Calorimeter) data therefor. Typically a polymer exhibits a narrow heat of fusion range distribution peak, indicating that all the polymer crystals thereof are of roughly the same morphology—i.e., have comparable heats of fusion so that they all soften at the same temperature. By way of contrast, smectic polymer contains some polymer chains that are highly crystallized and other polymer chains that are less highly crystalized. As a result, the smectic polymer exhibits a relatively wide range of heats of fusion, as evidenced by the relatively broad bell-shaped curve distribution (as opposed to the narrow peak distribution of non-smectic polymer). Indeed, the DSC curves for a smectic polymer typically indicate two peaks, a major peak and a minor peak within the major peak, while the DSC curves for a conventional non-smectic polymer exhibit only a single peak.

[0029] At this juncture, it should be appreciated that the distinction between the small polymer crystals and the relatively larger polymer crystals in the smectic material reflects not a difference in the molecular weights of the polymer crystals (i.e., the degree of polymerization thereof), but rather a difference in the morphology of the polymer crystals themselves. Typically the molten polymeric material which is passed through the spinnerette has polymer chains of generally the same molecular weight. Even where the pellets themselves are characterized by a wide molecular weight range, the initial processing thereof by heat and pressure in the spinnerette hopper acts to make them of a generally uniform molecular weight. Rather the “smectic crystallization” (or the “premature crystallization” or “supracrystallinity”), as applied to the present invention, relates to the morphology of the polymer crystals.

[0030] While various techniques may be used to achieve the premature crystallization of the fibers, it is most easily and economically achieved by rapid quenching of the fibers by liquid or gas cooling as the fibers leave the die of the spinnerette and approach the web of the collector. With the exception of the premature crystallization of the fibers during fabric formation, the production of the non-woven fabric according to the present invention is conventional in nature, and typically reflects well known non-woven fabric production techniques, especially those used in the production of meltblown fabrics. The quench temperature at which the molten filaments are quenched will depend, to some degree, on the composition of the molten polymer 30. For isotactic polypropylene a quench temperature of 23° C. or below is preferred.

[0031] The non-woven fabric thus produced is then calendered to compact the same. The roll surface temperature, roll surface pressure and roll speed of the calender are selected so as to soften the small polymer crystals (of relatively low heats of fusion), but not the relatively larger polymer crystals (of relatively higher heats of fusion), thereby to retain high vapor permeability while providing low liquid permeability. For example, a preferred smectic polypropylene meltblown fabric is calendered at a roll surface temperature of about 25 - 110° C., a roll surface pressure of 25-150 Newtons, and a roll speed of up to 200 meters per minute to form a medium 10 of the present invention.

[0032] Roll speeds in excess of 200 meters per minute typically do not provide adequate time for heating of the fabric passing through the calender nip. On the other hand, roll speed should be maintained at as high a level as possible in order to provide increased production rates.

[0033] Generally speaking, as the pressure and temperature of a calendering operation are increased, the crystallinity of the resultant medium (as measured by the increase of the area under the peaks of a DSC curve) also increases. If the temperature and pressure applied by the calendar are too low (or the roll speed too high), then the undercalendered meltblown fabric retains its high porosity to both liquid and gas and cannot act as a barrier sheet. If the temperature and pressure of the calender are too high (or the roll speed too low), then the overcalendered meltblown fabric is converted into a film which is totally impermeable to both gas and liquid (and noisy in use as well). Clearly, the optimum temperature, pressure and roll speed will depend on the nature of the particular smectic polymer being processed. While the degree of vapor permeability and liquid impermeability (hydrohead) will vary with the particular intended application of the product, typically a substantially complete liquid impermeability (even at a hydrostatic head of at least about 10 millibars) and a substantial complete vapor permeability (that is, a vapor permeability of at least about 1200 gm² @ 24 h) are preferred.

[0034] The preferred pressure and temperature parameters for the compacting step may be easily and rapidly determined for any quenched material by holding one of the temperatures and pressures variables constant, while varying the other variable. Generally, the higher compacting temperatures are required in order to obtain air permeabilities and MVTRs within the preferred ranges, and the higher compacting pressures are required to obtain higher hydroheads.

[0035] It will be appreciated that air permeability and moisture vapor transmission rates are not necessarily related. Air permeability is closely related to the compactness of the material being measured and its resistance to air flow therethrough, while MVTR is more related to the morphology of the material being measured and its resistance to moisture vapor transmission flow. Nonetheless, as a practical matter, air permeability measurements may be taken as indicative of MVTR measurements, subject to correction as necessary, where, for example, the MVTR measuring equipment is unavailable and the air permeability measuring equipment is available.

[0036] It is theorized that during calendering the small polymer crystals (with low heats of fusion) soften and act as a binder between the unsoftened larger polymer crystals (with high heats of fusion). It is theorized that the softening of the small polymer crystals allows them to close the pores between the large polymer crystals, thereby shrinking the fabric and forming a vapor permeable, liquid impermeable non-woven barrier medium. The calendering effects fiber shrinkage and contraction in the media, thereby closing the large liquid-bearing channels or pores therethrough while leaving open the relatively smaller vapor-bearing channels or pores therethrough.

[0037] The optimum balance of properties can be tailored for particular applications.

[0038] It will be appreciated by those skilled in the art that the term “calender,” as used herein, encompasses all means to perform both heat transfer and compacting (that is, heating and reducing the thickness of a fabric). While a calender is the most common mechanism for performing these operations, other mechanisms may be used instead or in addition thereto.

[0039] The media 10 is characterized by a hydrohead of at least about 10, and preferably at least 20 millibars, an MVTR of at least about 1200, and preferably at least 3000 g/m² @ 24 h, and an air permeability of about 0.1-100, and preferably 0.4-3 cfm. The laminated composite 16 (formed of the media 10 and a spunbond fabric 12) suitable for use as a backsheet in a diaper or other absorbent product, has a hydrohead of at least about 20, and preferably 30 millibars, an MVTR of at least about 2000, and preferably 4000 g/m² @ 24 h, and an air permeability of about 0.05-3, and preferably 0.1-1 cfm. These criteria are set forth in Table A below. TABLE A HYDROHEAD MVTR AIR PERMEABILITY mbr g/m² @24 h cfm Media ≧10 (≧20) ≧1,200 (≧3,000)  0.1-100 (0.4-3) Composite ≧20 (≧30) ≧2,000 (≧4,000) 0.05-3 (0.1-1)

[0040] With regard to the data of Table A, it will be appreciated that the upper limits on the air permeability exists because, if material has too high an air permeability, it will probably leak liquid as well as air. While there is no upper limit set for the moisture vapor transmission rate (MVTR), it is generally preferred that the MVTR not be so high as to produce a clammy feeling or chill due to a rapid evaporation of the water.

[0041] No upper limits are given for the hydrohead because, as a practical matter, no liquid permeability is desired, regardless of the amount of pressure being exerted on the liquid trapped by the media and/or composite. When the media and/or composite is used as the backsheet of an infant diaper, the pressure exerted thereon (that is, primarily the weight of the infant) will be minimal so that the indicated minimal values of the hydrohead for the media/composite are acceptable. On the other hand, when the media/composite is used as the backsheet of an adult diaper or an adult incontinence pad, clearly a much higher hydrohead is required to prevent the escape of liquid under the weight of the adult. Thus, for example, hydroheads of 120 millibars would be the minimum for a backsheet of an adult diaper intended for use by a 180 lb. person. It will be appreciated that the infant/adult difference will also play a role in the quantity of moisture (i.e., urine) which must be allowed to escape as moisture vapor, depending upon the size and health of the kidneys of the wearer. The MVTR rates set forth are appropriate for the accommodation of both infants and adults.

[0042] The products of the invention are characterized by a relatively high tensile strength (both MD and CD) relative to competitive products. A medium 10 according to the present invention was laminated on one side to a conventional spunbond fabric 12 and on the other side to a conventional meltblown fabric 14, to form a fabric 18 as illustrated in FIG. 1. The sample thus prepared had a hydrohead of 164 millibars and a moisture vapor transmission rate (MVTR) of 4411 g/m²/@ 24 h. In practical terms, the specimen exhibited essentially no liquid leakage and a very high moisture vapor permeability relative to other commercial diaper backsheet specimens of comparable basis weight.

[0043] Referring now to FIG. 2 in particular, FIG. 2A illustrates the formation of a thermally sensitive meltblown smectic web and FIG. 2B illustrates the compacting of the web and the optional lamination thereof to form an SM laminate 16.

[0044] Referring now to FIG. 2A in particular, the molten polymer 30 is extruded through a spinnerette or die hole 36 to form filaments 38. At the same time, hot air 40 is directed into the die body and emerges close to the filaments 38 being formed (adjacent the spinnerette) to draw the molten filaments 38. The molten filaments are then immediately quenched via chilled air 41 (for example, at about or below 23° C.) as they are fed into a quenching unit 42 via a fan 44 and piping 46 so that the drawn filaments 38 are prematurely quenched by the cold air, thereby resulting in the formation of a material containing both small polymer crystals and large polymer crystals. The prematurely quenched filaments 38 then fall onto a collector 50 comprised of a roll or a conveyer belt 52, under the influence of gravity and/or a suction box 54, to form a thermally sensitive meltblown smectic web 56. The meltblown web 56 is eventually collected on a take-up roll 58 for storage or used immediately in the next step of the process.

[0045] Referring now to FIG. 2B in particular, a thermally sensitive meltblown smectic web 56 is unwound from a supply drum 80A thereof at the unwinding station 80. The web is then passed through a compacting station 82. The compaction calender 82A of compacting station 82 has two rolls. The top roller has a smooth steel outer surface and thermal oil heating so as to provide a controlled temperature at the calender nip. The bottom roll is made of a softer material as compared to steel (e.g., a polyamide available under the trade name RACOLON) which make the media softer during compacting and prevents possible pinholes as the media gets thinner. The simultaneous heating and compression of the fabric fibers by the compaction calender 82A imparts liquid impermeability (barrier properties) to the medium of the present invention while retaining, at least to some degree, the gas permeability (breathability) thereof. The calendering effects fiber shrinkage and contraction in the media, (due to the heat effect of calendering) thereby closing the large liquid-bearing channels or pores therethrough while leaving open the relatively smaller vapor-bearing channels or pores therethrough. The output of compacting station 82 is a media 10 according to the present invention.

[0046] However, to enhance the strength and feel thereof, the media 10 is typically laminated together with at least one spunbond, spunmelt or other nonwoven fabric on one side thereof, and optionally a meltblown or second spunbond, spunmelt or other nonwoven fabric on the other side thereof. Thus, at unwinding station 82 a spunbond material 12 is unwound from a supply drum 83A thereof. The compacted meltblown media 10 and the spunbond material 12 are laminated together at a laminating station 84 by a lamination calender 84A to form a laminate 16.The lamination calender has a rubber-covered steel roll adjacent the media and an engraved roller adjacent the spunbond material.

[0047] Special roll combinations in the laminating station 84 may be used to affect the strength and textile-like softness (hand) of the final product, as well as adding desirable patterns to the fabric for aesthetic reasons. Preferably, the final product 16 (or 18 if a third layer is added) has a cloth-like feel combined with high tensile and related strength characteristics. The textile-like characteristics of the medium 10 are especially desirable where the fabric is used alone, although they may also be desirable when the medium 10 is used as an outer layer of a laminate.

[0048] In take-up station 85, the composite output 16 of lamination station 84 is wound on a take-up roll 85A.

[0049] In the description above and the examples below, the important variables were determined using internationally accepted tests as follows:

[0050] Hydrohead: EDANA-ERT-160-89

[0051] Air Permeability: EDANA-ERT-140.1-81

[0052] Mechanical (Tensile) Properties: EDANA-ERT-20.2-89

[0053] Basis Weight: EDANA-ERT-40.3-90

[0054] MVTR: ASTM-E96E

EXAMPLES Example I

[0055] In order to establish the porosity of a medium according to the present invention, a diaper backsheet made with a preferred product of the present invention was compared with the backsheets of several competitive commercial diapers, with the results provided below in Table I.

[0056] The backsheet product of the present invention (labeled “FQF” in Table 1) was a SMM fabric containing on one side 10 g/m² of spunbond fabric, in the middle 10 g/m² of smectic media compacted according to the present invention, and on the other side 10 g/m² of uncompressed meltblown fabric, for a total of 30 g/m². It was tested against diaper backsheets used in competitive commercial diapers available under the trade names HUGGIES/ULTRATRIM, HUGGIES/SUPREME, PAMPER/PREMIUM and DRYPERS/SUPREME.

[0057] All specimens were tested for hydrohead, MVTR, tensile strength (MD and CD) and percent elongation (MD and CD), and the data recorded in Table I.

[0058] The measurement of MVTR was accomplished by monitoring the amount of distilled water that evaporated through the specimen over a 24 hour period. The temperature of the water was maintained at 38° C. by using a constant temperature bath in which the jars of water were placed. A fan was used to maintain a constant air flow over the specimen. The height of the liquid was such that it did not interfere with the measurement as the top of the liquid was sufficiently above the bottom of the specimen.

[0059] The data of Table I shows that the hydrohead of a diaper backsheet made with the media according to the present invention (164) was second only to the Pamper/ Premium (192), and that the MVTR and percent elongation thereof (MD and CD) according to the present invention (164) exceeded all others. The tensile strength (MD and CD) of the media composite according to the present invention were comparable to those of the competitive products.

[0060] The data illustrate that a backsheet incorporating the media of the present invention as the barrier layer is comparable, or superior, to competitive products in all pertinent respects and, in particular, is greatly superior with respect to MVTR. Indeed, the MVTR of a backsheet according to the present invention is at least twice as high as the MVTR of the backsheets of the commercial products tested.

Example II

[0061] Three specimens were prepared from identical polypropylene pellets useful in the present invention. The first specimen was processed according to the present invention, including quenching and compacting. The second specimen was processed in the same manner, except that the quenching step and the compacting step were omitted. The third specimen was similarly processed, but with the quenching step being included and only the compacting step being omitted. The fourth and fifth specimens were similarly processed, but with the compacting step being included and only the quenching step being omitted. The fourth specimen was compacted at 75 N and 100° C., while the fifth specimen was compacted at 150 N and 110° C.

[0062] Pertinent data was collected at various points in the processing as reported in Table II below.

[0063] As might be expected, the material of specimen 2, a common meltblown, exhibited an air permeability of about 193 cfm, higher than the 100 cfm upper limit of acceptability. Similarly, the material of specimen 5, quenched and compacted at a high temperature, was a rigid, brittle film exhibiting a low hydrohead of 8 mm H₂O, relative to the lower limit of 10 mm H₂O for acceptability. Specimens 3 and 4 exhibited relatively high air permeabilities (83 cfm for specimen 3 and 36 cfm for specimen 4) such that they were within the limit for media according to the present invention as broadly defined (0.1-100 cfm), but substantially higher than the preferred limit (0.4-3 cfm). Further specimen 4 exhibited an unacceptably low MVTR, while specimens 3 and 5 were so porous to moisture vapor as to be out of the range of the available MVTR tester used.

[0064] The data illustrate that the quenching step alone or the compacting step alone are insufficient to produce a preferred medium according to the present invention. A preferred medium according to the present invention results only when both the quenching step and the compacting step are both performed.

[0065] The products of the present invention find utility in the healthcare industry, as discussed previously, as well as such diverse fields as clean room and health care gowns, clean room filters, house wraps, sterile packaging, battery separators and other industrial applications with barrier requirements which can be met by the product of the present invention.

[0066] For those applications which require a more elastomeric and more drapable media, without any change in the barrier properties or other advantages of the present invention, the molten polymer from which the media of the present invention is preferably made from a blend of 60-90% polypropylene and 10-40% polybutylene by weight. Media made from such a blend exhibit a higher elongation to break and are much more drapable as compared to those made from 100% polypropylene. Since such media are more elastic and behave more like rubber, laminates using such media exhibit lower noise (that is, less crinkling). A preferred polybutylene for use in the present invention is available under the trade name PB DP 8910PC from Montell Chemical Co.

[0067] It will be appreciated by those skilled in the art that the hydrohead test is of a static nature and measures only the ability of the barrier media to withstand a water pressure gradually applied thereto; this is sufficient for many applications. However, certain applications require a more dynamic test to determine the capacity of the barrier media to withstand an impact suddenly driving the water thereagainst. The dynamic liquid impact test mimics the dynamic load/area (energy) that a baby will impart to a saturated core/backsheet structure when abruptly going from a standing to a sitting position. The dynamic liquid impact (in g/m²) is calculated based on the impact energy that an average 20 lb. baby will impart to a saturated diaper if the baby “falls” onto it from a standing position. The baby is modeled as two rigid links of known mass and length, and the assumption is made that the links “fall” from rest, with the impact area being the region under the diaper. This works out to be approximately 20 Joules (14.75 ft.-lb.) over an average baby “seat” area of 13.5 in.² or about 2300 J/m². Dynamic liquid impact was measured according to a proprietary Dynamic Liquid Impact Test Method V-L-35 of Proctor & Gamble.

[0068] A single layer of non-porous film alone gives a test result of 0 g/m². A single layer of laminate using a media according to the present invention gives a test result of 547 g/m². A sample of two layers of such laminate gives a test result of 375-465 g/m².

[0069] For a diaper backsheet, test results of less than 700 g/m², preferably less than 550 g/m², are acceptable on a 30 gsm laminate sample consisting of a spunbond layer (10 gsm), a central layer of media according to the present invention (10 gsm), and a meltblown layer (10 gsm) laminate.

[0070] Thus, the media of the present invention exhibits acceptable test results on a dynamic impact liquid test. The dynamic impact liquid test results confirm that the media of the present invention is the limiting factor.

[0071] A sample made of two laminates (for example, each laminate having the media of the present invention in the center, a spunbond on one side thereof, and a meltblown on the other side thereof) typically exhibits a lower dynamic impact liquid test level than a sample made of a single laminate alone. It is theorized that this is due to the increased calendering of the media layers in the laminate affecting the morphology of the test material.

[0072] To summarize, the present invention provides a method of making a media of controlled porosity, combining high vapor permeability and low liquid permeability, which method does not require a specialized polymeric input or the use of chemical binders, additives or coating to provide the desired permeability. The present invention also provides material made by the aforesaid method, such material not producing noise during use, exhibiting cloth-like feel (hand), and being sufficiently economical to manufacture for use in disposable products.

[0073] Now that the preferred embodiments of the present invention have been shown and described in detail, various modifications and improvements thereon will become readily apparent to those skilled in the art. Accordingly, the spirit and scope of the present invention is to be construed broadly and limited only by the appended claims, and not by the foregoing specification. TABLE I Huggies/ Huggies/ Pamper/ Drypers/ Ultratrim Supreme Premium Supreme FQF Hydrohead 110 72 192 69 164 (mbar) MVTR 1495.5 1944.1 1198.4 1046.8 4411 g/m²/24 hrs MD 53.14 46.32 71.18 47.6 80.23 Tensile (N) CD Tensile 19.98 45.15 17.52 23.07 43.23 (N) MD Elong 30.4 53.6 107.13 52 40.85 % CD Elong 40.36 30.11 132.18 54.37 62.92 %

[0074] TABLE II Hydrohead MVTR Air Permeability Specimen mbar g/m² @ 24 hr cfm 1 59^(A) 4187 0.5 2 29^(A) — 193 3 40^(A) — 83 4 70^(C) 1148 36 5  8^(C) — 1 

We claim:
 1. A method of making a fibrous media combining high vapor permeability and low liquid permeability, the method comprising the steps of: (A) providing a non-woven fabric formed from fibers that are prematurely crystallized during fabric formation to form small polymer crystals therein having low heats of fusion and relatively larger polymer crystals therein of relatively higher heats of fusion; and (B) calendering the fabric to soften the small polymer crystals therein of low heats of fusion, but not the relatively larger polymer crystals therein of relatively higher heats of fusion, thereby to retain high vapor permeability while providing low liquid permeability.
 2. The method of claim 1 wherein the polymer is isotactic.
 3. The method of claim 1 wherein the polymer is polypropylene.
 4. The method of claim 1 wherein the polymer is a blend of polypropylene and polybutylene.
 5. The method of claim 4 wherein the blend is 60-90% polypropylene and 10-40% polybutylene by weight.
 6. The method of claim 1 wherein the polymer is isotactic polypropylene.
 7. The method of claim 1 wherein the polymer exhibits a bell-shaped heat of fusion range distribution prior to calendering.
 8. The method of claim 1 wherein the polymer is prematurely crystallized by quenching thereof prior to completion of fabric formation.
 9. The method of claim 1 wherein the temperature, pressure and roll speed of the calendering operation are selected to soften the small polymer crystals but not the relatively larger polymer crystals.
 10. The method of claim 9 wherein the fabric is calendered at a temperature of about 25 - 110° C., a pressure of about 25-150 Newtons, and a roll speed of up to about 200 meters/min.
 11. The method of claim 1 wherein the fabric is calendered in step (B) to retain a vapor permeability of at least 1200 g/m² @ 24h and provide a hydrohead of at least 10 millibars.
 12. The method of claim 1 including the step of forming a composite of the calendered material with at least one nonwoven fabric layer.
 13. The method of claim 12 including the step of forming a composite of the calendered material with at least one spunbond fabric layer.
 14. The method of claim 1 wherein the calendering effects fiber shrinkage and contraction in the fibrous media.
 15. The method of claim 1 wherein the nonwoven fabric is a meltblown.
 16. A method of making a non-woven fibrous media combining vapor permeability and low liquid impermeability, the method comprising the steps of: (A) providing a non-woven meltblown fabric formed of a polymer of isotactic polypropylene prematurely crystallized by quenching thereof prior to completion of fabric formation to form small polymer crystals therein having low heats of fusion and relatively larger polymer crystals therein of relatively higher heats of fusion; and (B) calendering the fabric to soften the small polymer crystals therein of low heats of fusion, but not the relatively larger polymer crystals therein of relatively higher heats of fusion, thereby to retain vapor permeability while providing liquid impermeability through fiber shrinkage and contraction in the fibrous media, the temperature, pressure and roll speed of the calendering operation being selected to soften the small polymer crystals but not the relatively larger polymer crystals.
 17. The method of claim 16 wherein the fabric is calendered at a temperature of about 25-110° C., a pressure of about 25-150 Newtons, and a roll speed of up to about 200 meters/minute, to retain a vapor permeability of at least about 1200 g/m² @ 24h and provide a hydrohead of at least about 10 millibars.
 18. The method of claim 16 including the step of forming a composite of the calendered material with at least one spunbond fabric layer.
 19. A non-woven fibrous media combining high vapor permeability and low liquid permeability, comprising: a non-woven fabric formed from fibers that are prematurely crystallized during fabric formation to form small polymer crystals therein having low heats of fusion and relatively larger polymer crystals therein of relatively higher heats of fusion, said fabric being calendered to soften said small polymer crystals, but not said relatively larger polymer crystals, thereby to retain high vapor permeability while providing low liquid permeability.
 20. The media of claim 19 wherein said polymer is isotactic.
 21. The media of claim 19 wherein said polymer is polypropylene.
 22. The media of claim 19 wherein the polymer is a blend of polypropylene and polybutylene.
 23. The media of claim 19 wherein the blend is 60-90% polypropylene and 10-40% polybutylene by weight.
 24. The media of claim 19 wherein said polymer is isotactic polypropylene.
 25. The media of claim 19 wherein, prior to calendering, said polymer exhibits a bell-shaped heat of fusion range distribution.
 26. The media of claim 19 wherein said polymer is prematurely crystallized by quenching thereof prior to completion of web formation.
 27. The media of claim 19 wherein the temperature, pressure and roll speed of the calendering operation are selected to soften said small polymer crystals but not said relatively larger polymer crystals.
 28. The media of claim 19 wherein said fabric is calendered in step (B) to retain a vapor permeability of at least 1200 g/m² @ 24h and provide a hydrohead of at least 10 millibars.
 29. The media of claim 19 wherein said non-woven fabric is a meltblown.
 30. A composite of the media of claim 19 with at least one spunbond fabric layer.
 31. A non-woven fibrous media formed from fibers that are prematurely crystallized during fabric formation and then calendered to yield a moisture vapor transmission rate greater than about 1,200 g/m² @ 24h and a hydrohead of at least about 10 millibars.
 32. The media of claim 31 having a moisture vapor transmission rate greater than about 3,000 g/m² @ 24h and a hydrohead of at least 20 millibars.
 33. A composite non-woven fabric formed from at least two non-woven layers, said composite having a MVTR of at least about 2,000 g/m² @ 24h and a hydrohead of at least about 20 millibars.
 34. The composite fabric of claim 33 having a MVTR of at least 4,000 g/m² @ 24h and a hydrohead of at least 30 millibars.
 35. The composite fabric of claim 33 wherein at least one of said non-woven layers is a spunbond.
 36. The composite fabric of claim 35 wherein at least one of said non-woven layers is formed of a prematurely crystallized and calendered meltblown fabric.
 37. The composite fabric of claim 36 in the nature of a diaper backsheet.
 38. The composite fabric of claim 33 having a dynamic liquid impact test result not exceeding 547 g/m². 